EPR Studies on Defect Production and lts Annealing Behavior in Silicon After High Fluence Ar lon lrradiation

Liu Changlong; Hou Mingdong; Cheng Song; Zhu Zhiyong; Wang Zhiguang; Sun Youmei; Jin Yunfan; Li Changlin

Chinese Physics C> 1998, Vol. 22> Issue(7) : 651-657

EPR Studies on Defect Production and lts Annealing Behavior in Silicon After High Fluence Ar lon lrradiation

Institute of Modern Physics,The Chinese Academy of Sciences,Lanzhou 730000

Abstract
HTML
Reference
Related

PDF

Abstract：
Silicon samples were irradiated below 50K with 1 12MeV Ar ions to a fluence of 8×10¹⁴/cm². Defect production and its isochronal annealing behavior have been investigated at room temperature by Electron Paramagnetic Resonance technique. Neutral 4-vacancy (Si-P3 center), positively charged 〈100〉 splitted di-interstitial (Si-P6 center) and the contiuous amorphous layer have been detected in the as-irradiated sample. At an annealing temperature of 200℃ , the Si-P3 and Si-P6 centers were annealed out and five vacancy cluster in negative charge state (Si-P1 center) began to grow. The Si-P1 center disappeared at about 550℃. For the temperature above 350℃, Si-A11 center (a center may include several vacancies) has been observed, which was stable up to 550℃, The temperatue for recrystallization of the continuous amorphous layer is higher than 600℃. During the annealing process, the line shape and line width for amorphous center were not changed. The results are qualitatively discussed.

References

[1]

Dennis J R, Hale E B. J. Appl. Phys., 1978, 49(3): 1119-1127[2] Murakami K, Masuda K, Gano K et al. Japan J. Appl. Phys., 1973, 12(9): 1307-1316[3] Cheng L J, Corelli J C, Corbett J W et al. Phys. Rev., 1966, 152(2):761--774[4] Varichenko V S, Zaitsev A M, Melnikov A A et al. Nucl. Instrum. Meths., 1994, B94:259-265[5] Nsenoff N, Fan H Y. Phys. Rev., 1962, 128(4): 1605-1613[6] Wun Jung, Newell G S. Phys. Rev., 1963, 132(2):648-662[7] Ohdomari I, Ikeda M, Yoshimoto H et al. Proc. Inter. Conf. on Ion Implantation in Semiconductor,Boulder Colordo: 1976, P39-46[8] Lee Y H, Gerasimenko N N, Corbett J W. Phys. Rev., 1976, B14:4506-4519[9] Lee Y H, Brosious P R, Corbett J W. Rad., Effs., 1974, 22: 169-172[10] Bogdanski P, Mary P, Toulemonde M. Nucl. Instrum. Meths., 1992, B62: 388-390[11] Liu Changlong, Hou Mingdong, zhu Zhiyong et al. High Energy Physics and Nuclear Physics, (in Chinese),1998, 22(9)(刘昌龙,侯明东,朱智勇等。高能物理与核物理,1998,22(9))

[1]	Fan Ying , REN Zhong-Zhou . Theoretical Studies on Electron Scattering of S and Si Isotopes. Chinese Physics C, 2006, 30(10): 983-987.
[2]	LUO Wen-Yun , WANG Chao-Zhuang , HE Xin-Fu , FAN Sheng , HUANG Xiao-Long , WANG Chuan-Shan . Non-ionizing Energy Loss of Middle Energy Proton in Si and GaAs. Chinese Physics C, 2006, 30(11): 1088-1090.
[3]	LIU Chang-Long , LU Yi-Ying , YIN LI . Effects of Additional Vacancy-Like Defects Produced by Ion Impealations on Boron Thermal Diffusion in Silicon. Chinese Physics C, 2005, 29(11): 1107-1111.
[4]	YANG Zhi-Hu , XIAO Guo-Qing , CHEN Xi-Meng , ZHANG Yan-Ping , ZHAO Yong-Tao , ZHANG Xiao-An , SU Hong , CUI Yin , ZHANG Hong-Qiang , XU Xu , SHAO Jian-Xiong . X-Ray in Highly Charged Ar¹⁷⁺Ion Interacting with Mo Surface. Chinese Physics C, 2004, 28(11): 1231-1233.
[5]	LIU Chang-Long . Effects of Si Ion Implantation and H Plasma Treatment on the Growth of Cavities in Silicon. Chinese Physics C, 2004, 28(9): 1013-1016.
[6]	WU Xiao-Shan , TAN Wei-Shi , JIANG Shu-Sheng , WU Zhong-Hua , DING Yong-Fan , . Microstructures of Ge/Si Superlattices Growtn at Low Temperature. Chinese Physics C, 2003, 27(8): 739-743.
[7]	HE Qing , JIA Quan-Jie , JIANG Xiao-Ming , CUI Jian , JIANG Zui-Min . Study of Si Caplayer Influence on Microstructure of Ge/Si Quantum Dots by Grazing Incident X-Ray Diffraction. Chinese Physics C, 2003, 27(S1): 49-52.
[8]	WANG Zhen-Xia , YU Li-Ping , ZHANG Wei , MA Yu-Gang , ZHU Zhi-Yuan , HE Guo-Wei , HU Gang , CHEN Yi . Nanoscale Ar-Bubbles Formed by Ions Irradiating Graphite. Chinese Physics C, 2002, 26(12): 1316-1319.
[9]	LIU Chang-Long . Effects of Ion Irradiation on the Diffusion of Pre-implanted B Atoms in Crystalline Silicon. Chinese Physics C, 2001, 25(12): 1238-1244.
[10]	LIU ChangLong , JIN YunFan , ZHU ZhiYong , SUN YouMei , HOU MingDong , WANG ZhiGuang , WANG YanBin , ZHANG ChongHong , CHEN XiaoXi , LIU Jie , LI BaoQuan . Infrared Absorption Study of Effects in Semicrystalline Polyethylene Terephthalate Films Induced by 35MeV/u Ar Ions. Chinese Physics C, 2000, 24(4): 352-358.
[11]	LIU ChangLong , JIN YunFan , ZHU ZhiYong , SUN YouMei , HOU MingDong , WANG YanBin , WANG ZhiGuang , ZHANG ChongHong , LIU Jie , CHEN XiaoXi , LI BaoQuan . Modifications in Optical Absorption of PET Films by High Energy Ar Ion Irradiation. Chinese Physics C, 2000, 24(7): 685-690.
[12]	Zhu Zhiyong , Hou Mingdong , Jin Yunfan , Li Changlin , Liu Changlong , Zhang Chonghong , Sun Youmei . Study of Defects in Silicon Irradiated With High Energy Ar Ions. Chinese Physics C, 1999, 23(12): 1248-1252.
[13]	Wang Zhenxia , Zhu Fuying , Wang Wenmin , Yu Guoqing , Ruan Meiling , Zhang Huiming , Zhu Jingping . Formation of Carbon Nanotubes in the Graphite Surface by Ar Ion Sputtering. Chinese Physics C, 1998, 22(12): 1182-1186.
[14]	Liu Changlong , Hou Mingdong , Zhu Zhiyong , Cheng Song , Li Baoquan , Sun Youmei , Wang Zhiguang , Jin Yunfan , Li Changlin , Wang Yinshu , Meng Qinghua . Paramagnetic Defect Production in Silicon After112MeV Ar Ion Irradiation. Chinese Physics C, 1998, 22(9): 858-863.
[15]	Liu Changlong , Hou Mingdong , Wang Zhiguang , Cheng Song , Sun Youmei , Zhu Zhiyong , Jin Yunfan , Li Changlin , Wang Yinshu , Meng Qinghua . Dimensional Changes of Amorphous Alloys Under Swift Ar Ion Irradiation. Chinese Physics C, 1997, 21(11): 1052-1056.
[16]	Liu Changlong , Hou Mingdong , Quan Mingxiu , Sun Wensheng . Study of Surface Blistering and Pinhole Formationon Argon Ion Bombarded Amorphous Alloys. Chinese Physics C, 1996, 20(8): 763-768.
[17]	Hou Mingdong , Liu Changlong , Quan Mingxiu , Sun Wensheng . Study of Topography Changes Induced by 150keV Argon Ion Bombardment of Amorphous Alloys. Chinese Physics C, 1994, 18(S1): 33-38.
[18]	ZHU Guo-Yi , HE Jing-Tang , GU Yi-Fan , QIAN Zhong-Min , CHU Guo-Zhu . STUDY ON RADIATION DAMAGE OF CHINESE-MADE HIGH-Z SCINTILLATION CRYSTALS. Chinese Physics C, 1990, 14(1): 8-15.
[19]	SHEN Wen-Qing , YIN Shu-Zhi , GUO Zhong-Yan , ZHU Yong-Tai , CHEN Ju-Shen , WU En-Jiu , GUO Chi-Di , FENG En-Pu , XIE Yuan-Xiang . A MEASUREMENT OF THE ELASTIC SCATTERING FOR REACTION ¹²C+²⁸Si AT ENERGIES 56MeV—69MeV. Chinese Physics C, 1984, 8(5): 628-632.
[20]	LU CHANG-GUO , . EPR PARADOX AND ITS EXPERIMENTAL TEST. Chinese Physics C, 1983, 7(6): 665-673.

Access

Get Citation

Liu Changlong, Hou Mingdong, Cheng Song, Zhu Zhiyong, Wang Zhiguang, Sun Youmei, Jin Yunfan and Li Changlin. EPR Studies on Defect Production and lts Annealing Behavior in Silicon After High Fluence Ar lon lrradiation[J]. Chinese Physics C, 1998, 22(7): 651-657.

RIS(for EndNote,Reference Manager,ProCite)

BibTex

Txt

Milestone

Received: 1900-01-01
Revised: 1900-01-01

Article Metric

Article Views(4033)
PDF Downloads(526)
Cited by(0)

Policy on re-use

To reuse of subscription content published by CPC, the users need to request permission from CPC, unless the content was published under an Open Access license which automatically permits that type of reuse.

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

EPR Studies on Defect Production and lts Annealing Behavior in Silicon After High Fluence Ar lon lrradiation

Corresponding author: Liu Changlong,

Institute of Modern Physics,The Chinese Academy of Sciences,Lanzhou 730000

Received Date: 1900-01-01

Accepted Date: 1900-01-01

Available Online: 1998-07-05

Abstract: Silicon samples were irradiated below 50K with 1 12MeV Ar ions to a fluence of 8×10¹⁴/cm². Defect production and its isochronal annealing behavior have been investigated at room temperature by Electron Paramagnetic Resonance technique. Neutral 4-vacancy (Si-P3 center), positively charged 〈100〉 splitted di-interstitial (Si-P6 center) and the contiuous amorphous layer have been detected in the as-irradiated sample. At an annealing temperature of 200℃ , the Si-P3 and Si-P6 centers were annealed out and five vacancy cluster in negative charge state (Si-P1 center) began to grow. The Si-P1 center disappeared at about 550℃. For the temperature above 350℃, Si-A11 center (a center may include several vacancies) has been observed, which was stable up to 550℃, The temperatue for recrystallization of the continuous amorphous layer is higher than 600℃. During the annealing process, the line shape and line width for amorphous center were not changed. The results are qualitatively discussed.

HTML

Reference (1)

EPR Studies on Defect Production and lts Annealing Behavior in Silicon After High Fluence Ar lon lrradiation

Abstract：

References

Access

Article Metrics

Metrics

通讯作者: 陈斌, bchen63@163.com

Email This Article